CNC plasma cutting machines are widely used in the modern machinery processing industry. The choice of process parameters has a very important influence on the cutting quality, cutting speed, cutting efficiency and cutting effect. The correct use of CNC plasma cutting machine for high-quality rapid cutting, must be mastered and understood the cutting process parameters. The following is the technical personnel of Wuhan Baba-resistant CNC, for the majority of customers from cutting current and cutting speed, analyze the importance of CNC plasma cutting machine process parameters:
One of the process parameters: cutting current
Cutting current: It is the most important cutting process parameters that directly determine the cutting thickness and speed, ie cutting ability.
Impact:
1. The cutting current increases, the arc energy increases, the cutting ability increases, and the cutting speed increases.
2. The cutting current increases, the diameter of the arc increases, and the arc becomes thicker so that the incision becomes wider;
3. When the cutting current is too large, the thermal load of the nozzle increases, the nozzle is damaged prematurely, and the cutting quality naturally decreases, and even normal cutting cannot be performed. Therefore, the cutting current and the corresponding nozzle should be selected correctly according to the thickness of the material before cutting.
Process parameter two: cutting speed
Cutting speed: The optimal cutting speed range can be selected according to equipment instructions or determined by tests. Due to the thickness and material of the material, the melting point, the thermal conductivity and the surface tension after melting, the cutting speed is also corresponding. Variety.
main performance:
1. Moderately improved cutting speed can improve the quality of the incision, that is, the incision is slightly narrowed, the incision surface is more even and the deformation can be reduced.
2. If the cutting speed is too fast, the energy of the cutting line is lower than the required amount. The jet in the slit cannot quickly blow off the melted cutting melt to form a large rear drag, accompanied with slag, incision Surface quality declines.
3. When the cutting speed is too low, because the cutting point is the anode of the plasma arc, in order to maintain the stability of the arc itself, the anode spot or anode area must find the conducting current place near the nearest kerf to the arc, and it will also flow toward the jet. Radiating more heat, so that the incision widens, melted material on both sides of the incision gathered and solidified at the bottom edge, forming a slag difficult to clean, and the upper edge of the incision due to excessive melting and heating to form a rounded corner.
4. When the speed is extremely low, the arc will even extinguish due to the wide cut. Thus, good cutting quality and cutting speed are inseparable.
Select cutting machine to China cutting machine trading network, let you buy the rest assured! A variety of CNC cutting machine and CNC cutting equipment, a variety of cutting machine models, let the optional! Official website: /
1.Welding materials
In Welding, substances called filler materials or consumables are used. As the name implies, these substances provide filler or a body of molten materials that provides a strong bond to be formed between the base metals used. Most welding processes will also require some form of shielding to protect both the main components and filler from being oxidized during the process.
The type of welding materials used during welding depends on the nature of the job intended. Electrodes draw the necessary energy in order to perform welding applications. Luoyang Golden Egret Company has any kind of welding materials include CTC Welding Rod /rope, SCTC welding rod/rope, TC electronic welding rod, Ni-based welding rod, flux-cored Welding Wires, solid welding wires and etc.
Welding can be applied in different kinds of industries such as building and construction, oil and gas, marine, power generation, steel, mine tools, automobile, transportation and etc.
2. Welding rod
1)Cast tungsten carbide based tubular rod
The hard phase of the rod is cast tungsten carbide which leads to higher hardness and better wear-resistance.
Wear resistance: the wear resistance is 6-7 times better than others. Tested by ASTM G65
Mainly used for Mining machinery, Geological tools, Petroleum drilling tools etc, by Oxy-Acetylene with weak carburizing flame.
Product recommendation:
GT1103 (CTC, 60-80 mesh),
GT1103-1(CTC, 20-30 um),
GT1103-2(CTC, 40-60 um)
2)The hard phase of tube rod is carbide pellets which leads to higher impact resistance and better wear resistance than CTC cloase rod.
Wear resistance: the wear resistance is 6-7 times better than others. Tested by ASTM G65 wear test.
Mainly used for mining machinery. Geological tools etc; by Oxy-acetylene with weak carburizing flame.
Product recommendation:
GT2102 (Cemented carbide grit, 30-60mesh)
GT2102-2(Cemented carbide grit, 30-40mesh)
GT2102-3(Cemented carbide grit, 40-60mesh)
3)Tube rod is composited by Cemented carbide pellets, Spherical CTC and CTC. The layer has higher impact resistance, better wear resistance and good fluidity than other rods.
Wear resistance: the wear resistance is 6-7 times better than others. Tested by ASTM G65.
Mainly used for oil method drill bits, such as Tri-cone bit, Steel tooth bit, PDC bit, etc. By Oxy-Acetylene with weak carburizing flame.
Product recommendation:
GT3302 (carbide pellets, 20-40mesh)
GT3302-1(carbide pellets, 14-40um)
4)The hard phase of the rod is monocrystal WC, the welding layer has a higher wear resistance and better impact resistance.
The wear resistance is 6-7 times better than others, tested by ASTM G65 method.
Mainly used for the repair and strength for oil drills bits, such as PDC bit diameter holding by Oxy-Acetylene with weak carburizing flame.
Product recommendation:
GT4104 (Monocrystal WC, 80-200mesh)
3. Welding Rope
Made form mixture of CTC and self-fluxing nickel alloy covering on nickel wire. The CTC is in spherical or irregular with good wear resistance; the nickel alloy is in spherical or nearly spherical shape with good wettability and erosion resistance and better corrosion resistance than tubular rod.
Recommend to use Petroleum drilling tools, Concrete mixing blade, Mud pump, Coal sluice, Coal drill pipe, Tunnel drilling machinery etc.
By Oxy-Acetylene Welding with weak carburizing flame.
Product recommendation:
GS110450N (CTC, 4mm, HRC 47-55)
GS110550N (CTC, 5mm, HRC 47-55)
GS110650N (CTC, 6mm, HRC 47-55)
4. Welding Bar
The rod is sintered by CTC and Ni-based powders. The CTC(Cast Tungsten Carbide) is in irregular or spherical shape with better wear resistance and the nickel alloy is in spherical or nearly spherical shape and has good wettability with cast tungsten carbide. The cladding layer has a higher impact resistance and better wear resistance.
Its wear resistance and corrosion resistance is between tube rod and flexible rope.
Mainly used on the Steel PDC bit, Concrete mixer blade, Mud pump, Miner chute, Miner drill stem and Mechanical parts of Tunnel rock drill machine etc.
Welded by Oxy-Acetylene with weak carburizing flame.
Product recommendation:
GD4025253-3(CTC, SCTC, 4*600/6*600)
GD4030303-3(CTC, SCTC, 4*600/6*600)
5. Welding wire
Intensified molybdenum titanium vanadium composite chromium carbide welding wire can improve layer`s bonding strength and tenacity. This wire can use for multilayer welding which has no peel off, and it can maintain good wear resistance under certain impact working condition.
Product recommendation:GSQD671Mo-4(1.6mm)
Medium carbon and high chromium wear resistance welding wire has a higher hardness, stronger wear resistance, and excellent toughness by adding a certain amount of molybdenum alloys and boride. It has a better impact resistance and strip resistance than high chromium cast iron type materials
Product recommendation: GSQD621Mo-4(1.6mm)
With high sphericity & excellent alloy organization, cemented carbide pellet is mainly used in welding, as an adding material of PTA Powder , tubular welding rod, to improve the wear resistance of the workpieces greatly.
Product recommendation: GQ06
Cemented carbide grit with different percent of cobalt has good abrasive resistance and is widely used for making grinding, polishing and cutting tools.
Product recommendation: GS08A
Weld Materials,Tubular Welding Rod,Welding Electrodes,Stainless Steel Welding Rod