High wear resistance Alumina ceramic V guide wheel /bearing

Feature
Alumina Ceramic has the advantages of super hardness,high wear-resisting,good corrosion resistance ,high temperature tolerance,precision process, high mechanical strength, good chemical stability,good  smoothness, mechanical seal good, and so on.
 
Property

Items
Unit
95%Al2O3
99.5%Al2O3

Density
g/cm3
3.7
3.9

Flexural Strength
MPa
313
340

Compressive Strength
MPa
3400
3600

Modulus of Elasticity
GPa
350
380

Impact Resistance
MPa·m1/2
4
5.1

Weibull Modulus
m
10
10

Vickers Hardness
HV0.5
1800
1900

Thermal Conductivity
W/mk
24
27

Highest Application Temperature
°C
1600
1750

Volume Resistivity at 20°C
Ω.cm20
>1014
>1014

Dielertric strength
KV/mm
20
25

Thermal expansion
X10-6/K
5.0-8.3
         5.4-8.3

 

 
Forming methods includes
 
  1,Drying pressing
  2,Isostatic pressing
  3,Hot pressing casting
 
The application of our product
 
    1, Ceramic shaft for aquatic animals equipment filter pump
    2, Ceramic plunger for high pressure cleaner.
    3,Wearlessness,resistant acid-base and high intensity ceramic  assembly apply to petroleum ,chemical and chemical industry.
    4,Wearlesness, corrosion resistance parts apply to precision machine. High wear resistance Alumina ceramic V guide wheel /bearing

Feature
Alumina Ceramic has the advantages of super hardness,high wear-resisting,good corrosion resistance ,high temperature tolerance,precision process, high mechanical strength, good chemical stability,good  smoothness, mechanical seal good, and so on.
 
Property

Items
Unit
95%Al2O3
99.5%Al2O3

Density
g/cm3
3.7
3.9

Flexural Strength
MPa
313
340

Compressive Strength
MPa
3400
3600

Modulus of Elasticity
GPa
350
380

Impact Resistance
MPa·m1/2
4
5.1

Weibull Modulus
m
10
10

Vickers Hardness
HV0.5
1800
1900

Thermal Conductivity
W/mk
24
27

Highest Application Temperature
°C
1600
1750

Volume Resistivity at 20°C
Ω.cm20
>1014
>1014

Dielertric strength
KV/mm
20
25

Thermal expansion
X10-6/K
5.0-8.3
         5.4-8.3

 

 
Forming methods includes
 
  1,Drying pressing
  2,Isostatic pressing
  3,Hot pressing casting
 
The application of our product
 
    1, Ceramic shaft for aquatic animals equipment filter pump
    2, Ceramic plunger for high pressure cleaner.
    3,Wearlessness,resistant acid-base and high intensity ceramic  assembly apply to petroleum ,chemical and chemical industry.
    4,Wearlesness, corrosion resistance parts apply to precision machine.

Double-Toothed Roll Crusher

A double-toothed Roll Crusher is a type of crusher that uses two parallel toothed rollers to crush materials. It is designed for crushing materials such as coal, limestone, coke, etc., with a compressive strength of less than 240MPa and a moisture content of less than 35%.

The double-toothed roll crusher is composed of two toothed rollers, which rotate in opposite directions. The teeth on the rollers are arranged in a staggered pattern, which ensures that the materials are crushed evenly. The rollers are supported by bearings, and the gap between the rollers can be adjusted to control the size of the crushed materials.

The double-toothed roll crusher has several advantages over other types of crushers. First, it has a simple structure and is easy to operate. Second, it can crush materials with a higher moisture content than other types of crushers. Third, it produces a uniform product size, which is important for many applications.

Double-Toothed Roll Crusher,Winner Double Toothed Roll Crusher

SiChuan TieYing Machinery Manufacturing CO.,LTD; , https://www.tieyingcrushers.com